Ti6246钛合金 β → α 相变中晶界 α 相生长行为及其对微织构的影响 |
齐敏, 王倩, 马英杰, 曹贺萌, 黄森森, 雷家峰, 杨锐 |
Growth Behavior of Grain Boundary α Phase and Its Effect on the Microtexture During β → α Phase Transformation in Ti6246 Titanium Alloys |
QI Min, WANG Qian, MA Yingjie, CAO Hemeng, HUANG Sensen, LEI Jiafeng, YANG Riu |
图9 Ti6246合金由β单相区炉冷至880 ℃后多个位置α相晶粒的EBSD分析 |
Fig.9 EBSD analyses of the α phase grain at multiple positions (a-d) of Ti6246 alloy after furnace cooling from β phase field to 880 oC, pole overlaps as shown in black boxes |
![]() |