Ti6246钛合金 β → α 相变中晶界 α 相生长行为及其对微织构的影响 |
齐敏, 王倩, 马英杰, 曹贺萌, 黄森森, 雷家峰, 杨锐 |
Growth Behavior of Grain Boundary α Phase and Its Effect on the Microtexture During β → α Phase Transformation in Ti6246 Titanium Alloys |
QI Min, WANG Qian, MA Yingjie, CAO Hemeng, HUANG Sensen, LEI Jiafeng, YANG Riu |
图1 β退火热处理和中断炉冷热处理制度示意图 |
Fig.1 Schematics of the heat treatment processes (T—temperature, t—time, F.C.—furnace cooling, W.Q.—water quenching, Tβ —β-transus temperature) (a) β annealing treatment (b) interrupted furnace cooling treatment |
![]() |