FGH96合金静态再结晶过程的显微组织演化
Evolution of Microstrucutre During Static Recrystallization in FGH96 Superalloy
(a) 1100 oC (b) 1120 oC (c) 1140 oC (d) 1160 oC (e) 1180 oC (f) 1260 oC
FGH96合金静态再结晶过程的显微组织演化 |
| 彭子超, 罗俊鹏, 赵宇, 周磊, 王旭青, 邹金文 |
|
Evolution of Microstrucutre During Static Recrystallization in FGH96 Superalloy |
| PENG Zichao, LUO Junpeng, ZHAO Yu, ZHOU Lei, WANG Xuqing, ZOU Jinwen |
| 图3 不同温度固溶处理后FGH96合金的TEM像 |
| Fig.3 TEM images of FGH96 superalloy with different solution temperatures (a) 1100 oC (b) 1120 oC (c) 1140 oC (d) 1160 oC (e) 1180 oC (f) 1260 oC |
|
|