电弧熔丝增材制造<strong>Mg/Mg</strong>双金属的组织与力学性能

电弧熔丝增材制造Mg/Mg双金属的组织与力学性能

韩启飞, 狄兴隆, 郭跃岭, 叶水俊, 郑元翾, 刘长猛

Microstructure and Mechanical Properties of Mg/Mg Bimetals Fabricated by Wire Arc Additive Manufacturing

HAN Qifei, DI Xinglong, GUO Yueling, YE Shuijun, ZHENG Yuanxuan, LIU Changmeng

表2 Mg-Al-Si/Mg-Gd-Y-Zn双金属WAAM工艺参数

Table 2 Process parameters of WAAM Mg-Al-Si/Mg-Gd-Y-Zn bimetal

Alloy

$I_{p}$

A

f

Hz

$t_{p}$

%

$I_{p}$ / $I_{b}$

%

$V_{s}$

mm·min^-1

$V_{w}$

cm·min^-1

H

mm

$V_{a}$

L·min^-1

$U_{a}$

V

Mg-Al-Si

122

1.5

25

16

150

150

1.3

20

20

Remelting Mg-Al-Si

150

1.5

20

15

150

090

1.3

20

19

Mg-Gd-Y-Zn

122

1.5

25

16

150

090

1.3

20

20