室温和深冷轧制对纯<strong>Al</strong>再结晶<strong>{111}/{111}</strong>近奇异晶界的影响

室温和深冷轧制对纯Al再结晶{111}/{111}近奇异晶界的影响

李振想, 王卫国, Rohrer Gregory S, 洪丽华, 陈松, 林燕, 周邦新

Effects of Ambient and Cryogenic Rolling on {111}/{111} Near Singular Boundary Formation During Subsequent Recrystallization Annealing in Pure Aluminum

LI Zhenxiang, WANG Weiguo, Rohrer Gregory S, HONG Lihua, CHEN Song, LIN Yan, ZHOU Bangxin

图13 {011}< $01 \bar{1}$ >取向晶粒(P1和P2)与{011}< $01 \bar{1}$ >漫散取向晶粒M及其他取向晶粒N之间形成{111}/{111}-NSB的晶胞示意图

Fig.13 Schematics of unit cell showing the formation of {111}/{111}-NSB abutted by {011}< $01 \bar{1}$ > oriented grain (P1 and P2) with grain M of {011}< $01 \bar{1}$ > diffusive orientation (a) and grain N of other orientation (b)表7 {011}< $01 \bar{1}$ >取向晶粒(P1和P2)与{011}< $01 \bar{1}$ >漫散取向晶粒M及其他取向晶粒N的取向信息及其关联晶界的取向差信息(对应图13)