室温和深冷轧制对纯<strong>Al</strong>再结晶<strong>{111}/{111}</strong>近奇异晶界的影响

室温和深冷轧制对纯Al再结晶{111}/{111}近奇异晶界的影响

李振想, 王卫国, Rohrer Gregory S, 洪丽华, 陈松, 林燕, 周邦新

Effects of Ambient and Cryogenic Rolling on {111}/{111} Near Singular Boundary Formation During Subsequent Recrystallization Annealing in Pure Aluminum

LI Zhenxiang, WANG Weiguo, Rohrer Gregory S, HONG Lihua, CHEN Song, LIN Yan, ZHOU Bangxin

图11 {011}< $01 \bar{1}$ >取向晶粒与其他取向晶粒间形成{111}/{111}-NSB的显微组织OIM图和{111}重叠极图晶界迹线分析

Fig.11 {111}/{111}-NSB (GB_GJ, GB_HK, and GB_IL) formed between {011}< $01 \bar{1}$ > oriented grains (grains G, H, and I) and other oriented grains (grains J, K, and L)
(a-c) OIM images (d-f) {111} overlapped pole figure grain boundary trace analyses