室温和深冷轧制对纯<strong>Al</strong>再结晶<strong>{111}/{111}</strong>近奇异晶界的影响

室温和深冷轧制对纯Al再结晶{111}/{111}近奇异晶界的影响

李振想, 王卫国, Rohrer Gregory S, 洪丽华, 陈松, 林燕, 周邦新

Effects of Ambient and Cryogenic Rolling on {111}/{111} Near Singular Boundary Formation During Subsequent Recrystallization Annealing in Pure Aluminum

LI Zhenxiang, WANG Weiguo, Rohrer Gregory S, HONG Lihua, CHEN Song, LIN Yan, ZHOU Bangxin

图10 经室温和深冷轧制后再经370 ℃退火不同时间各样品的ODF截面图

Fig.10 Orientation distribution function (ODF) sections (φ₂ = 45º) of the samples annealed at 370 ^oC for varied time after rolling at room temperature and cryo-temperature (Φ, φ₁, φ₂—Euler angles)
(a) sample B (b) sample D (c) sample F
(d) sample B1 (e) sample D1 (f) sample F1