室温和深冷轧制对纯Al再结晶{111}/{111}近奇异晶界的影响
Effects of Ambient and Cryogenic Rolling on {111}/{111} Near Singular Boundary Formation During Subsequent Recrystallization Annealing in Pure Aluminum
室温和深冷轧制对纯Al再结晶{111}/{111}近奇异晶界的影响 |
| 李振想, 王卫国, Rohrer Gregory S, 洪丽华, 陈松, 林燕, 周邦新 |
|
Effects of Ambient and Cryogenic Rolling on {111}/{111} Near Singular Boundary Formation During Subsequent Recrystallization Annealing in Pure Aluminum |
| LI Zhenxiang, WANG Weiguo, Rohrer Gregory S, HONG Lihua, CHEN Song, LIN Yan, ZHOU Bangxin |
| 图8 轧制样品及轧制后370 ℃退火样品的Vickers硬度 |
| Fig.8 Vickers hardnesses of the rolled samples and the samples annealed at 370 oC for varied time after rolling |
|
|