室温和深冷轧制对纯Al再结晶{111}/{111}近奇异晶界的影响

李振想, 王卫国, Rohrer Gregory S, 洪丽华, 陈松, 林燕, 周邦新

Effects of Ambient and Cryogenic Rolling on {111}/{111} Near Singular Boundary Formation During Subsequent Recrystallization Annealing in Pure Aluminum

LI Zhenxiang, WANG Weiguo, Rohrer Gregory S, HONG Lihua, CHEN Song, LIN Yan, ZHOU Bangxin

图6 轧制样品及轧制后370 ℃退火样品的{022}XRD谱

Fig.6 XRD spectra of the rolled samples and the samples annealed at 370 oC for varied time after rolling (a) {022}diffraction peaks of the samples A, A1, B, B1, and powder (θi —diffraction angle of sample i) (b) {022} diffraction peaks of samples A-F and A1-F1