室温和深冷轧制对纯<strong>Al</strong>再结晶<strong>{111}/{111}</strong>近奇异晶界的影响

室温和深冷轧制对纯Al再结晶{111}/{111}近奇异晶界的影响

李振想, 王卫国, Rohrer Gregory S, 洪丽华, 陈松, 林燕, 周邦新

Effects of Ambient and Cryogenic Rolling on {111}/{111} Near Singular Boundary Formation During Subsequent Recrystallization Annealing in Pure Aluminum

LI Zhenxiang, WANG Weiguo, Rohrer Gregory S, HONG Lihua, CHEN Song, LIN Yan, ZHOU Bangxin

图4 F1样品中存在{111}/{111}-NSB的各组晶界的GBPD图(投影在(001)内)

Fig.4 GBPD maps of the grain boundaries with varied misorientations containing {111}/{111}-NSB in sample F1
(a) [111]/15° (b) [111]/25° (c) [111]/30° (d) [111]/35° (e) [111]/40° (f) [111]/45°
(g) [111]/50° (h) [111]/55° (i) [112]/25° (j) [122]/20° (k) [122]/25° (l) [122]/30°
(m) [122]/35° (n) [122]/40°