过冷(Fe1 -x Co x)79.3B20.7 合金的凝固
杨林, 马长松, 刘连杰, 李金富

Solidification of Undercooled (Fe1 -x Co x)79.3B20.7 Alloys
YANG Lin, MA Changsong, LIU Lianjie, LI Jinfu
图9 (Fe1 - x Co x)79.3B20.7合金各初生相析出的临界过冷度范围及其与Co含量的关系
Fig.9 Undercooling ranges for various primary phases to precipitate and their dependences on the Co content in (Fe1 - x Co x)79.3B20.7 alloys (ΔTM2B, ΔTM23B6, and ΔTα represent the critical undercoolings above which M2B, M23B6, and α-M/M3B precipitate as primary phases, respectively)