热处理工艺和W丝特性对W丝增强锆基非晶复合材料残余应力的影响
Effects of Heat Treatment Processes and W Wire Properties on Residual Stress in W Wire Reinforced Zr-Based Metallic Glass Composites
热处理工艺和W丝特性对W丝增强锆基非晶复合材料残余应力的影响 |
| 李彪, 张龙, 颜廷毅, 付华萌, 袁旭东, 文明月, 张宏伟, 李宏, 张海峰 |
|
Effects of Heat Treatment Processes and W Wire Properties on Residual Stress in W Wire Reinforced Zr-Based Metallic Glass Composites |
| LI Biao, ZHANG Long, YAN Tingyi, FU Huameng, YUAN Xudong, WEN Mingyue, ZHANG Hongwei, LI Hong, ZHANG Haifeng |
| 图3 不同热处理工艺条件下以直径0.2 mm未烧氢W丝作为增强相的非晶复合材料轴向和径向的中子衍射数据精修结果 |
| Fig.3 Refinement results of axial (a) and radial (b) neutron diffraction data of metallic glass composites with 0.2 mm-diameter W wires not-annealed in hydrogen as reinforcement phase under different heat treatment process conditions (Q—scattering factor, Rwp—weighted graphical variance factor, Obs—observation, Calc—calculation, Bkg—background) |
|
|