M50钢中 M2C一次碳化物高温转变机制

马芳, 陆星宇, 周丽娜, 杜宁宇, 类承帅, 刘宏伟, 李殿中

High-Temperature Decomposition Mechanism of M2C Primary Carbide in M50 Steel

MA Fang, LU Xingyu, ZHOU Lina, DU Ningyu, LEI Chengshuai, LIU Hongwei, LI Dianzhong

表4 图4中M2C与MC碳化物的EDS结果 (mass fraction / %)

Table 4 EDS results of M2C and MC carbides in Fig.4

Carbide Point Fe Cr Mo V C M2C 1 5.61 9.07 58.87 14.72 11.73 2 6.68 9.49 55.82 14.54 13.47 3 5.90 10.52 57.07 13.57 12.94 4 6.87 9.53 56.20 14.60 12.80 5 5.84 8.96 57.77 14.10 13.33 MC 6 3.03 5.56 38.34 33.54 19.53 7 2.79 5.61 38.34 37.49 15.77 8 5.27 5.50 35.33 38.32 15.58