马芳, 陆星宇, 周丽娜, 杜宁宇, 类承帅, 刘宏伟, 李殿中

High-Temperature Decomposition Mechanism of M2C Primary Carbide in M50 Steel

MA Fang, LU Xingyu, ZHOU Lina, DU Ningyu, LEI Chengshuai, LIU Hongwei, LI Dianzhong

表3 图2c中块状一次碳化物的EDS结果 (mass fraction / %)

Table 3 EDS results of the block-like carbide in Fig.2c

Point Fe Cr Mo V C 1 8.02 11.75 55.09 12.62 12.52 2 8.73 11.76 54.51 12.59 12.41 3 6.29 12.71 56.14 12.46 12.40 4 9.04 12.03 54.35 12.47 12.11 5 10.28 12.47 53.46 11.61 12.18