M50钢中 M2C一次碳化物高温转变机制

马芳, 陆星宇, 周丽娜, 杜宁宇, 类承帅, 刘宏伟, 李殿中

High-Temperature Decomposition Mechanism of M2C Primary Carbide in M50 Steel

MA Fang, LU Xingyu, ZHOU Lina, DU Ningyu, LEI Chengshuai, LIU Hongwei, LI Dianzhong

表2 图2b中棒状一次碳化物的EDS结果 (mass fraction / %)

Table 2 EDS results of the rod-like carbide in Fig.2b

Point Fe Cr Mo V C 1 26.06 14.12 41.12 9.17 9.41 2 34.51 10.07 38.97 8.23 8.23 3 33.48 9.38 39.61 7.99 9.32 4 36.25 9.73 38.17 7.70 8.15 5 22.93 10.34 45.77 11.22 8.64