M50钢中 M2C一次碳化物高温转变机制

马芳, 陆星宇, 周丽娜, 杜宁宇, 类承帅, 刘宏伟, 李殿中

High-Temperature Decomposition Mechanism of M2C Primary Carbide in M50 Steel

MA Fang, LU Xingyu, ZHOU Lina, DU Ningyu, LEI Chengshuai, LIU Hongwei, LI Dianzhong

表1 图2a中片层状一次碳化物的EDS结果 (mass fraction / %)

Table 1 EDS results of the lamellar-like carbide in Fig.2a

Point Fe Cr Mo V C 1 26.19 12.19 40.49 9.71 11.42 2 22.82 10.18 45.05 10.15 11.80 3 17.17 11.32 47.99 11.37 12.15 4 22.41 10.96 44.75 10.30 11.58 5 21.41 11.71 44.40 11.16 11.32