TC19合金铸锭中Zr、Mo元素的宏观偏析行为
Macrosegregation of Zr and Mo in TC19 Titanium Alloy Ingot
(a) R = 3 mm/h (b) R = 6 mm/h (c) R = 15 mm/h
(d) R = 30 mm/h (e) R = 60 mm/h (f) R = 150 mm/h
TC19合金铸锭中Zr、Mo元素的宏观偏析行为 |
| 朱绍祥, 王清江, 刘建荣, 陈志勇 |
|
Macrosegregation of Zr and Mo in TC19 Titanium Alloy Ingot |
| ZHU Shaoxiang, WANG Qingjiang, LIU Jianrong, CHEN Zhiyong |
| 图4 TC19合金不同凝固速率定向凝固样品低倍组织 |
| Fig.4 Macrostructures of directionally solidified TC19 alloy samples at various withdrawal rates (R) (BZ—base zone, UGZ—uniform growth zone, RSZ—rapid separation zone) (a) R = 3 mm/h (b) R = 6 mm/h (c) R = 15 mm/h (d) R = 30 mm/h (e) R = 60 mm/h (f) R = 150 mm/h |
|
|