AlSi10Mg多孔结构在不同加载应变率下的损伤模式及响应机制
Damage Modes and Response Mechanisms of AlSi10Mg Porous Structures Under Different Loading Strain Rates
(a) initial status (b) first fracture (ε ≈ 8.7%) (c) serious damage (ε ≈ 25%)
AlSi10Mg多孔结构在不同加载应变率下的损伤模式及响应机制 |
| 蔡宣明, 张伟, 范志强, 高玉波, 王俊元, 张柱军 |
|
Damage Modes and Response Mechanisms of AlSi10Mg Porous Structures Under Different Loading Strain Rates |
| CAI Xuanming, ZHANG Wei, FAN Zhiqiang, GAO Yubo, WANG Junyuan, ZHANG Zhujun |
| 图7 AlSi10Mg多孔结构在中应变率(50 s-1)加载条件下的变形破坏模式及破坏位置示意图 |
| Fig.7 Deformation failure mode (a-c) and schematic of damage location (dash line) (d) of AlSi10Mg porous structure under medium strain rate loading (50 s-1) (a) initial status (b) first fracture (ε ≈ 8.7%) (c) serious damage (ε ≈ 25%) |
|
|