高Cr马氏体耐热钢的协同强化机制及形变热处理应用
Synergistic Strengthening of High-Cr Martensitic Heat-Resistant Steel and Application of Thermo-Mechanical Treatments
(a, b) MX particles (c, d) Cu-rich particles
高Cr马氏体耐热钢的协同强化机制及形变热处理应用 |
| 张竟文, 余黎明, 刘晨曦, 丁然, 刘永长 |
|
Synergistic Strengthening of High-Cr Martensitic Heat-Resistant Steel and Application of Thermo-Mechanical Treatments |
| ZHANG Jingwen, YU Liming, LIU Chenxi, DING Ran, LIU Yongchang |
| 图8 初始态和20%冷轧态G115钢回火不同时间后沉淀相与位错之间的交互作用及650℃、160 MPa下的蠕变应变-时间曲线[ |
| Fig.8 Interactions between precipitates and dislocations of initial state and 20% cold-rolled G115 steel after tempering for different time (a-d) and creep strain versus time curves obtained at 650oC under 160 MPa (e)[ (a, b) MX particles (c, d) Cu-rich particles |
|
|