不同条件下纳米晶 α-Zr蠕变行为的分子动力学模拟
Molecular Dynamics Simulation of Creep Mechanism in Nanocrystalline α-Zirconium Under Various Conditions
(a) 373 K-5 keV (b) 573 K-5 keV (c) 773 K-5 keV
(d) 373 K-10 keV (e) 573 K-10 keV (f) 773 K-10 keV
不同条件下纳米晶 α-Zr蠕变行为的分子动力学模拟 |
| 孟子凯, 孟智超, 高长源, 郭辉, 陈汉森, 陈刘涛, 徐东生, 杨锐 |
|
Molecular Dynamics Simulation of Creep Mechanism in Nanocrystalline α-Zirconium Under Various Conditions |
| MENG Zikai, MENG Zhichao, GAO Changyuan, GUO Hui, CHEN Hansen, CHEN Liutao, XU Dongsheng, YANG Rui |
| 图16 不同温度-M4-5 GPa-PKA能量的级联体系在蠕变终态(300 ps)时的晶体结构 |
| Fig.16 Crystal structures of the M4-5 GPa cascaded systems at the final state of creep process (300 ps) (a) 373 K-5 keV (b) 573 K-5 keV (c) 773 K-5 keV (d) 373 K-10 keV (e) 573 K-10 keV (f) 773 K-10 keV |
|
|