超音速微粒轰击诱导表面纳米化对300M钢腐蚀疲劳行为的影响
Effect of Surface Nanocrystallization Induced by Supersonic Fine Particles Bombardment on Corrosion Fatigue Behavior of 300M Steel
超音速微粒轰击诱导表面纳米化对300M钢腐蚀疲劳行为的影响 |
| 熊毅, 栾泽伟, 马云飞, 厉勇, 查小琴 |
|
Effect of Surface Nanocrystallization Induced by Supersonic Fine Particles Bombardment on Corrosion Fatigue Behavior of 300M Steel |
| XIONG Yi, LUAN Zewei, MA Yunfei, LI Yong, ZHA Xiaoqin |
| 图5 SFPB处理前后300M钢腐蚀疲劳应力-寿命(S-N)曲线 |
| Fig.5 Corrosion fatigue stress-life (S-N) curves of 300M steel without and with SFPB treatment (Nf—cycle to failure, σmax—maximum stress) |
|
|