700℃时效对9Cr ODS钢微观组织和力学性能的影响

汪建强, 刘威峰, 刘生, 徐斌, 孙明月, 李殿中

Effect of Aging Treatment at 700oC on Microstructure and Mechanical Properties of 9Cr ODS Steel

WANG Jianqiang, LIU Weifeng, LIU Sheng, XU Bin, SUN Mingyue, LI Dianzhong

表1 图8f中颗粒P1~P3的EDS结果

Table 1 EDS results of particles P1-P3 in Fig.8f (mass fraction / %)

Point Fe Cr W C Ti Y P1 40.85 44.84 11.30 2.95 0.06 0.00 P2 65.80 30.48 2.92 0.68 0.12 0.01 P3 40.99 47.31 10.16 1.33 0.21 0.00