700℃时效对9Cr ODS钢微观组织和力学性能的影响
Effect of Aging Treatment at 700oC on Microstructure and Mechanical Properties of 9Cr ODS Steel
700℃时效对9Cr ODS钢微观组织和力学性能的影响 |
| 汪建强, 刘威峰, 刘生, 徐斌, 孙明月, 李殿中 |
|
Effect of Aging Treatment at 700oC on Microstructure and Mechanical Properties of 9Cr ODS Steel |
| WANG Jianqiang, LIU Weifeng, LIU Sheng, XU Bin, SUN Mingyue, LI Dianzhong |
| 图8 9Cr ODS钢初始态及在700℃时效不同时间后的室温拉伸断口形貌 |
| Fig.8 Tensile fracture morphologies (at room temperature) of as-HIPed 9Cr ODS steel (a); and aged at 700oC for 50 h (b), 200 h (c), 1000 h (d), and 3000 h (e, f) |
|
|