Nb锆合金在含氧蒸汽中耐腐蚀性能恶化的机理
黄建松, 裴文, 徐诗彤, 白勇, 姚美意, 胡丽娟, 谢耀平, 周邦新

Degradation Mechanism on Corrosion Resistance of High Nb-Containing Zirconium Alloys in Oxygen-Containing Steam
HUANG Jiansong, PEI Wen, XU Shitong, BAI Yong, YAO Meiyi, HU Lijuan, XIE Yaoping, ZHOU Bangxin
图10 图9b和c中所示的SPP1~SPP3第二相HRTEM像及FFT分析
Fig.10 HRTEM images and FFT analyses (insets) of SPPs marked in Figs.9b and c, including SPP1 (a-c), SPP2 (d-f), and SPP3 (g-h1), wherein magnifications of regions B, C (b, c), E, F (e, f), H (h), and FFT analysis corresponding to the region in Fig.10h (h1)