高Nb锆合金在含氧蒸汽中耐腐蚀性能恶化的机理
Degradation Mechanism on Corrosion Resistance of High Nb-Containing Zirconium Alloys in Oxygen-Containing Steam
高Nb锆合金在含氧蒸汽中耐腐蚀性能恶化的机理 |
| 黄建松, 裴文, 徐诗彤, 白勇, 姚美意, 胡丽娟, 谢耀平, 周邦新 |
|
Degradation Mechanism on Corrosion Resistance of High Nb-Containing Zirconium Alloys in Oxygen-Containing Steam |
| HUANG Jiansong, PEI Wen, XU Shitong, BAI Yong, YAO Meiyi, HU Lijuan, XIE Yaoping, ZHOU Bangxin |
| 图5 合金在400℃、10.3 MPa的DE过热蒸汽中腐蚀42 d的氧化膜横截面HAADF像及对应元素的EDS面分布图 |
| Fig.5 HAADF images and corresponding EDS mapping of the complete region (a) and region 1 magnification (b) of cross-sectional oxide film on the alloy corroded in superheated steam with DE at 400oC and 10.3 MPa for 42 d |
|
|