初始组织及冷轧压下量对工业低牌号电工钢相变织构及磁性能的影响
Influence of Initial Microstructure and Cold Rolling Reduction on Transformation Texture and Magnetic Properties of Industrial Low-Grade Electrical Steel
(a, b) 0.50 mm, 75% reduction (c, d) 0.20 mm, 90% reduction
初始组织及冷轧压下量对工业低牌号电工钢相变织构及磁性能的影响 |
| 杨平, 马丹丹, 顾晨, 顾新福 |
|
Influence of Initial Microstructure and Cold Rolling Reduction on Transformation Texture and Magnetic Properties of Industrial Low-Grade Electrical Steel |
| YANG Ping, MA Dandan, GU Chen, GU Xinfu |
| 图11 不同热轧样品经不同压下量冷轧后在1100℃保温7 min相变退火的样品的磁性能 |
| Fig.11 Iron loss (P1.5) (a, c) and magnetic induction (B50) (b, d) of transformation annealed samples at 1100oC for 7 min after different cold rolling processes in hot rolling processes A-E, respectively (TD—transverse direction) (a, b) 0.50 mm, 75% reduction (c, d) 0.20 mm, 90% reduction |
|
|