初始组织及冷轧压下量对工业低牌号电工钢相变织构及磁性能的影响
Influence of Initial Microstructure and Cold Rolling Reduction on Transformation Texture and Magnetic Properties of Industrial Low-Grade Electrical Steel
初始组织及冷轧压下量对工业低牌号电工钢相变织构及磁性能的影响 |
| 杨平, 马丹丹, 顾晨, 顾新福 |
|
Influence of Initial Microstructure and Cold Rolling Reduction on Transformation Texture and Magnetic Properties of Industrial Low-Grade Electrical Steel |
| YANG Ping, MA Dandan, GU Chen, GU Xinfu |
| 图10 低温热轧样品(D工艺)冷轧后1000℃退火5 min的EBSD取向成像图与ODF图(φ2 = 45°) |
| Fig.10 IPF-Z maps (a, b) and ODF figures (φ2 = 45°) (c, d) for through thickness cross section of annealed samples at 1000oC for 5 min after different cold rolling processes in the hot rolling process D (a, c) 0.60 mm, 70% reduction (b, d) 0.20 mm, 90% reduction |
|
|