初始组织及冷轧压下量对工业低牌号电工钢相变织构及磁性能的影响
Influence of Initial Microstructure and Cold Rolling Reduction on Transformation Texture and Magnetic Properties of Industrial Low-Grade Electrical Steel
初始组织及冷轧压下量对工业低牌号电工钢相变织构及磁性能的影响 |
| 杨平, 马丹丹, 顾晨, 顾新福 |
|
Influence of Initial Microstructure and Cold Rolling Reduction on Transformation Texture and Magnetic Properties of Industrial Low-Grade Electrical Steel |
| YANG Ping, MA Dandan, GU Chen, GU Xinfu |
| 图3 4种热轧样品和1种柱状晶初始样品经冷轧(0.50 mm、75%压下量)后1100℃保温7 min相变退火的EBSD取向成像图和ODF图(φ2 = 45°) |
| Fig.3 IPF-Z maps (a-e) and ODF figures (φ2 = 45°) (f-j) for through thickness cross section of annealed samples at 1100oC for 7 min after cold rolling (0.50 mm, 75% reduction) in the hot rolling processes A (a, f), B (b, g), C (c, h), D (d, i), and E (e, j), respectively |
|
|