微米级选区激光熔化316L不锈钢的拉伸力学性能
|
|
张楠, 张海武, 王淼辉
|
Tensile Mechanical Properties of Micro-Selective Laser Melted 316L Stainless Steel
|
|
ZHANG Nan, ZHANG Haiwu, WANG Miaohui
|
|
表2 图8b和e中Σ3晶界分析结果
|
Table 2 Σ3 grain boundary analysis results in Figs.8b and e
|
|
| No. | φ / (o) | Type | No. | φ / (o) | Type |
|---|
| 8b-1 | +4 | IC | 8e-1 | +8 | IC | | 8b-2 | -2 | C | 8e-2 | -1 | C | | 8b-3 | +6 | IC | 8e-3 | -2 | C | | 8b-4 | +2 | C | 8e-4 | 0 | C | | 8b-5 | 0 | C | 8e-5 | -2 | C | | 8b-6 | -6 | IC | 8e-6 | +4 | IC | | 8b-7 | +4 | IC | 8e-7 | -3 | C | | 8b-8 | -1 | C | 8e-8 | +3 | C | | 8b-9 | +7 | IC | 8e-9 | -9 | IC | | 8b-10 | -3 | C | 8e-10 | -2 | C | | 8b-11 | -5 | IC | 8e-11 | -7 | IC | | 8b-12 | +3 | C | 8e-12 | -2 | C | | 8b-13 | -7 | IC | 8e-13 | +1 | C | | 8b-14 | +2 | C | 8e-14 | -4 | IC | | 8b-15 | -6 | IC | 8e-15 | +7 | IC | | 8b-16 | -3 | C | 8e-16 | +1 | C | | 8b-17 | +9 | IC | 8e-17 | -2 | C | | 8b-18 | -6 | IC | 8e-18 | +5 | IC | | 8b-19 | +3 | C | 8e-19 | +1 | C | | 8b-20 | +4 | IC | 8e-20 | -2 | C | | 8b-21 | +1 | C | 8e-21 | -3 | C | | 8b-22 | -5 | IC | 8e-22 | +5 | IC | | 8b-23 | +6 | IC | 8e-23 | +1 | C | | 8b-24 | -4 | IC | 8e-24 | 0 | C | | 8b-25 | -1 | C | 8e-25 | -1 | C | | 8b-26 | 0 | C | 8e-26 | +2 | C | | 8b-27 | +7 | IC | 8e-27 | -2 | C | | 8b-28 | -5 | IC | 8e-28 | +3 | C | | 8b-29 | -6 | IC | 8e-29 | +1 | C | | 8b-30 | -2 | C | 8e-30 | +4 | IC |
|
|
|