A2BTi型磁性功能合金相稳定性、磁性与力学性能的第一性原理计算和实验研究
Phase Stability, Magnetism, and Mechanical Properties of A2BTi: First-Principles Calculations and Experimental Studies
A2BTi型磁性功能合金相稳定性、磁性与力学性能的第一性原理计算和实验研究 |
| 杨谨菡, 闫海乐, 刘昊轩, 赵莹, 杨一俏, 赵骧, 左良 |
|
Phase Stability, Magnetism, and Mechanical Properties of A2BTi: First-Principles Calculations and Experimental Studies |
| YANG Jinhan, YAN Haile, LIU Haoxuan, ZHAO Ying, YANG Yiqiao, ZHAO Xiang, ZUO Liang |
| 图4 Co2NiTi、Fe2NiTi和Ni2CoTi合金磁化强度-温度(M(T))曲线以及DSC曲线 |
| Fig.4 Temperature-dependent magnetization (M(T)) (a1-c1) and DSC (a2-c2) curves for Co2NiTi (a1, a2), Fe2NiTi (b1, b2), and Ni2CoTi (c1, c2) alloys (Inset in Fig.4a1 is an enlarged M(T) curve at the low-temperature range under the magnetic field interlity H = 0.01 T; insets in Figs.4a2-c2 are the DSC curves measured at the high-temperature range (300 K to the melting point). ZFC—zero-field-cooling, ZC—field-cooling, FH—field-heating) |
|
|