强磁场下过冷Cu-Co/Cu-Co-Fe合金的凝固组织和摩擦性能
Solidification Microstructure and Wear Properties of Undercooled Cu-Co/Cu-Co-Fe Alloys Under a High Magnetic Field
强磁场下过冷Cu-Co/Cu-Co-Fe合金的凝固组织和摩擦性能 |
| 魏晨, 王军, 闫育洁, 范嘉懿, 李金山 |
|
Solidification Microstructure and Wear Properties of Undercooled Cu-Co/Cu-Co-Fe Alloys Under a High Magnetic Field |
| WEI Chen, WANG Jun, YAN Yujie, FAN Jiayi, LI Jinshan |
| 图3 不同磁场强度不同过冷度下Cu52Co24Fe24合金的凝固组织 |
| Fig.3 OM images of microstructures of the Cu52Co24Fe24 alloys solidified at different ΔT and magnetic fields (a-j) and SE-SEM images of the boxed regions in Figs.3a-j, respectively (a1-j1) (a, a1) 0 T, ΔT = 45 K (b, b1) 0 T, ΔT = 224 K (c, c1, d, d1) 5 T, ΔT = 86 K (e, e1, f, f1) 5 T, ΔT = 244 K (g, g1, h, h1) 10 T, ΔT = 110 K (i, i1, j, j1) 10 T, ΔT = 254 K |
|
|