晶粒长大对高纯Al {111}/{111}近奇异晶界的影响
Effects of Grain Growth on the {111}/{111} Near Singular Boundaries in High Purity Aluminum
晶粒长大对高纯Al {111}/{111}近奇异晶界的影响 |
| 冯小铮, 王卫国, Gregory S. Rohrer, 陈松, 洪丽华, 林燕, 王宗谱, 周邦新 |
|
Effects of Grain Growth on the {111}/{111} Near Singular Boundaries in High Purity Aluminum |
| FENG Xiaozheng, WANG Weiguo, Gregory S. Rohrer, CHEN Song, HONG Lihua, LIN Yan, WANG Zongpu, ZHOU Bangxin |
| 图2 再结晶高纯Al在500℃保温不同时间后的OIM图和取向差分布 |
| Fig.2 OIM (a-c) and misorientation distributions (d-f) of high purity aluminum heated at 500oC for 1 min (a, d), 5 min (b, e), and 30 min (c, f) after recrystallization (Solid areas show the uneven grain size zones, and dashed areas show the microtexture zones) |
|
|