K439B铸造高温合金800℃长期时效组织与性能演变 |
||||||||||||||||||||||||
张雷雷, 陈晶阳, 汤鑫, 肖程波, 张明军, 杨卿 | ||||||||||||||||||||||||
Evolution of Microstructures and Mechanical Properties of K439B Superalloy During Long-Term Aging at 800oC |
||||||||||||||||||||||||
ZHANG Leilei, CHEN Jingyang, TANG Xin, XIAO Chengbo, ZHANG Mingjun, YANG Qing | ||||||||||||||||||||||||
表2 K439B合金800℃时效不同时间后枝晶间及晶界区域M23C6碳化物的含量 |
||||||||||||||||||||||||
Table 2 Contents of M23C6 carbide in the interdendritic region and at grain boundary of K439B alloy subjected to long-term aging at 800oC |
||||||||||||||||||||||||
|
||||||||||||||||||||||||