K439B铸造高温合金800℃长期时效组织与性能演变
Evolution of Microstructures and Mechanical Properties of K439B Superalloy During Long-Term Aging at 800oC
K439B铸造高温合金800℃长期时效组织与性能演变 |
| 张雷雷, 陈晶阳, 汤鑫, 肖程波, 张明军, 杨卿 |
|
Evolution of Microstructures and Mechanical Properties of K439B Superalloy During Long-Term Aging at 800oC |
| ZHANG Leilei, CHEN Jingyang, TANG Xin, XIAO Chengbo, ZHANG Mingjun, YANG Qing |
| 图10 K439B合金800℃长期时效不同时间后815℃、379 MPa持久断口附近位错形貌 |
| Fig.10 Dislocation structures near 815oC, 379 MPa stress rupture fracture surface of K439B alloy subjected to long-term aging at 800oC for 0 h (a-c) and 3000 h (d-f) |
|
|