K439B铸造高温合金800℃长期时效组织与性能演变
Evolution of Microstructures and Mechanical Properties of K439B Superalloy During Long-Term Aging at 800oC
K439B铸造高温合金800℃长期时效组织与性能演变 |
| 张雷雷, 陈晶阳, 汤鑫, 肖程波, 张明军, 杨卿 |
|
Evolution of Microstructures and Mechanical Properties of K439B Superalloy During Long-Term Aging at 800oC |
| ZHANG Leilei, CHEN Jingyang, TANG Xin, XIAO Chengbo, ZHANG Mingjun, YANG Qing |
| 图2 K439B合金800℃长期时效不同时间后枝晶干部位γ′相的典型形貌SEM像 |
| Fig.2 Typical microstructures of γ′ precipitates in the dendrite core of K439B alloy subjected to long-term aging at 800oC for 0 h (a), 100 h (b), 500 h (c), 1000 h (d), 2000 h (e), and 3000 h (f) |
|
|