新型钴基高温合金中W元素对蠕变组织和性能的影响
陈佳, 郭敏, 杨敏, 刘林, 张军

Effects of W Concentration on Creep Microstructure and Property of Novel Co-Based Superalloys
CHEN Jia, GUO Min, YANG Min, LIU Lin, ZHANG Jun
图4 不同应变下的二阶不变矩密度谱(SOMIM)
Fig.4 Second order moment invariant maps (SOMIM) for 8W (a1-a4), 9W (b1-b4), and 10W (c1-c4) at strains of 1.0% (a1-c1), 1.5% (a2-c2), 2.0% (a3-c3), and 3.0% (a4-c4) (ω¯1, ω¯2—second order moment invariants)