不同温度轧制Al-Zn-Mg-Cu合金再结晶后的{111}/{111}近奇异晶界
{111}/{111} Near Singular Boundaries in an Al-Zn-Mg-Cu Alloy Recrystallized After Rolling at Different Temperatures
不同温度轧制Al-Zn-Mg-Cu合金再结晶后的{111}/{111}近奇异晶界 |
| 王宗谱, 王卫国, Rohrer Gregory S, 陈松, 洪丽华, 林燕, 冯小铮, 任帅, 周邦新 |
|
{111}/{111} Near Singular Boundaries in an Al-Zn-Mg-Cu Alloy Recrystallized After Rolling at Different Temperatures |
| WANG Zongpu, WANG Weiguo, Rohrer Gregory S, CHEN Song, HONG Lihua, LIN Yan, FENG Xiaozheng, REN Shuai, ZHOU Bangxin |
| 图8 Al-Zn-Mg-Cu合金包含{111}/{111}-NSB微区OIM像、{111}/{111}-NSB的{111}重叠极图晶界迹线分析和{111}/{111}-NSB离线原位表面侵蚀形貌特征 |
| Fig.8 OIM images of the areas containing {111}/{111}-NSB (a, d), grain boundary trace analyses for {111}/{111}-NSB based on {111} overlapped pole figures (b, e), and morphologies of {111}/{111}-NSB after off-line in-situ surface etching (c, f) (LAGB—low angle grain boundary, RB—random boundary, A—grain A, B—grain B, C—grain C, D—grain D) (a-c) {111}/{111}-NSB (GBAB) with a misorientation of [1 |
|
|