不同温度轧制Al-Zn-Mg-Cu合金再结晶后的{111}/{111}近奇异晶界
{111}/{111} Near Singular Boundaries in an Al-Zn-Mg-Cu Alloy Recrystallized After Rolling at Different Temperatures
不同温度轧制Al-Zn-Mg-Cu合金再结晶后的{111}/{111}近奇异晶界 |
| 王宗谱, 王卫国, Rohrer Gregory S, 陈松, 洪丽华, 林燕, 冯小铮, 任帅, 周邦新 |
|
{111}/{111} Near Singular Boundaries in an Al-Zn-Mg-Cu Alloy Recrystallized After Rolling at Different Temperatures |
| WANG Zongpu, WANG Weiguo, Rohrer Gregory S, CHEN Song, HONG Lihua, LIN Yan, FENG Xiaozheng, REN Shuai, ZHOU Bangxin |
| 图7 样品A~C的Σ3 (<111>/60°)晶界的五参数晶界面分布图(投影在(001)内) |
| Fig.7 Five parameter grain boundary plane distributions of Σ3 (<111>/60°) boundaries in the samples A (a), B (b), and C (c) |
|
|