不同温度轧制Al-Zn-Mg-Cu合金再结晶后的{111}/{111}近奇异晶界

王宗谱, 王卫国, Rohrer Gregory S, 陈松, 洪丽华, 林燕, 冯小铮, 任帅, 周邦新

{111}/{111} Near Singular Boundaries in an Al-Zn-Mg-Cu Alloy Recrystallized After Rolling at Different Temperatures

WANG Zongpu, WANG Weiguo, Rohrer Gregory S, CHEN Song, HONG Lihua, LIN Yan, FENG Xiaozheng, REN Shuai, ZHOU Bangxin

图5 样品C不同取向差{111}/{111}-NSB的五参数晶界面分布图(投影在(001)内)

Fig.5 Five parameter grain boundary plane distributions of {111}/{111}-NSB with varied misorientations in the sample C (a) [111]/20° (b) [111]/25° (c) [111]/30° (d) [111]/50° (e) [122]/20° (f) [122]/25° (g) [122]/35°