不同温度轧制Al-Zn-Mg-Cu合金再结晶后的{111}/{111}近奇异晶界
{111}/{111} Near Singular Boundaries in an Al-Zn-Mg-Cu Alloy Recrystallized After Rolling at Different Temperatures
(a) [111]/20° (b) [111]/45° (c) [111]/50° (d) [112]/30° (e) [122]/35°
不同温度轧制Al-Zn-Mg-Cu合金再结晶后的{111}/{111}近奇异晶界 |
| 王宗谱, 王卫国, Rohrer Gregory S, 陈松, 洪丽华, 林燕, 冯小铮, 任帅, 周邦新 |
|
{111}/{111} Near Singular Boundaries in an Al-Zn-Mg-Cu Alloy Recrystallized After Rolling at Different Temperatures |
| WANG Zongpu, WANG Weiguo, Rohrer Gregory S, CHEN Song, HONG Lihua, LIN Yan, FENG Xiaozheng, REN Shuai, ZHOU Bangxin |
| 图3 样品A不同取向差{111}/{111}近奇异晶界(NSB)的五参数晶界面分布图(投影在(001)内) |
| Fig.3 Five parameter grain boundary plane distributions of {111}/{111} near singular boundary (NSB) with varied misorientations in the sample A (MRD—multiple of random distribution) (a) [111]/20° (b) [111]/45° (c) [111]/50° (d) [112]/30° (e) [122]/35° |
|
|