不同温度轧制Al-Zn-Mg-Cu合金再结晶后的{111}/{111}近奇异晶界
{111}/{111} Near Singular Boundaries in an Al-Zn-Mg-Cu Alloy Recrystallized After Rolling at Different Temperatures
(a) rotation around <111> (b) rotation around <112> (c) rotation around <122>
不同温度轧制Al-Zn-Mg-Cu合金再结晶后的{111}/{111}近奇异晶界 |
| 王宗谱, 王卫国, Rohrer Gregory S, 陈松, 洪丽华, 林燕, 冯小铮, 任帅, 周邦新 |
|
{111}/{111} Near Singular Boundaries in an Al-Zn-Mg-Cu Alloy Recrystallized After Rolling at Different Temperatures |
| WANG Zongpu, WANG Weiguo, Rohrer Gregory S, CHEN Song, HONG Lihua, LIN Yan, FENG Xiaozheng, REN Shuai, ZHOU Bangxin |
| 图2 样品A~E的固定转轴晶界取向差分布 |
| Fig.2 Misorientation distributions of grain boundaries with specific rotation axes for the samples A-E (a) rotation around <111> (b) rotation around <112> (c) rotation around <122> |
|
|