9%Cr合金钢在含Cl－环境中的初期腐蚀行为及局部腐蚀起源
Initial Corrosion Behavior and Local Corrosion Origin of 9%Cr Alloy Steel in Cl－Containing Environment
9%Cr合金钢在含Cl－环境中的初期腐蚀行为及局部腐蚀起源 |
| 陈润农, 李昭东, 曹燕光, 张启富, 李晓刚 |
|
Initial Corrosion Behavior and Local Corrosion Origin of 9%Cr Alloy Steel in Cl－Containing Environment |
| CHEN Runnong, LI Zhaodong, CAO Yanguang, ZHANG Qifu, LI Xiaogang |
| 图14 9Cr钢在2%NaCl溶液中浸泡300 min后的典型局部腐蚀形貌及元素分布 |
| Fig.14 Local corrosion morphologies (a, b) of 9Cr steel immersed in 2%NaCl solution for 300 min and main element distributions (c, d) around a corrosion pit in Fig.14b (Inset in Fig.14a shows the corresponding high magnified image) |
|
|