9%Cr合金钢在含Cl－环境中的初期腐蚀行为及局部腐蚀起源
Initial Corrosion Behavior and Local Corrosion Origin of 9%Cr Alloy Steel in Cl－Containing Environment
9%Cr合金钢在含Cl－环境中的初期腐蚀行为及局部腐蚀起源 |
| 陈润农, 李昭东, 曹燕光, 张启富, 李晓刚 |
|
Initial Corrosion Behavior and Local Corrosion Origin of 9%Cr Alloy Steel in Cl－Containing Environment |
| CHEN Runnong, LI Zhaodong, CAO Yanguang, ZHANG Qifu, LI Xiaogang |
| 图5 9Cr钢腐蚀360 h后锈层截面的EPMA面扫描图 |
| Fig.5 Cross-sectional morphology (a) and EPMA elemental mappings (b-e) of the cross-sectional rust layer of 9Cr steel after corrosion for 360 h |
|
|