Fe22Cr5Al3Mo-xY合金在模拟LOCA下的高温蒸汽氧化行为
High-Temperature Steam Oxidation Behavior of Fe22Cr5Al3Mo-xY Alloy Under Simulated LOCA Condition
Fe22Cr5Al3Mo-xY合金在模拟LOCA下的高温蒸汽氧化行为 |
| 孙蓉蓉, 姚美意, 王皓瑜, 张文怀, 胡丽娟, 仇云龙, 林晓冬, 谢耀平, 杨健, 董建新, 成国光 |
|
High-Temperature Steam Oxidation Behavior of Fe22Cr5Al3Mo-xY Alloy Under Simulated LOCA Condition |
| SUN Rongrong, YAO Meiyi, WANG Haoyu, ZHANG Wenhuai, HU Lijuan, QIU Yunlong, LIN Xiaodong, XIE Yaoping, YANG Jian, DONG Jianxin, CHENG Guoguang |
| 图4 0Y和0.15Y合金在1000和1200℃高温蒸汽条件下恒温2 h的氧化膜截面显微组织的高角环形暗场(HAADF)像(图3中虚线位置) |
| Fig.4 High-angle annular dark field (HAADF) images of the cross-sectional oxide films formed on the 0Y (a, b) and 0.15Y (c, d) alloys oxidized in 1000oC (a, c) and 1200oC (b, d) steam for 2 h (the positions of dotted line in Fig.3) (Region indicated by arrow in Fig.4c stands for pores, the area of D1 in Fig.4d stands for the HAADF image of the cross-sectional angular oxide in Fig.3d) |
|
|