初始晶粒尺寸和强化相对GH4096高温合金热变形行为和再结晶的影响
Effects of Initial Grain Size and Strengthening Phase on Thermal Deformation and Recrystallization Behavior of GH4096 Superalloy
(a) 30% engineering strain (b) 50% engineering strain (c, d) 70% engineering strain
初始晶粒尺寸和强化相对GH4096高温合金热变形行为和再结晶的影响 |
| 李福林, 付锐, 白云瑞, 孟令超, 谭海兵, 钟燕, 田伟, 杜金辉, 田志凌 |
|
Effects of Initial Grain Size and Strengthening Phase on Thermal Deformation and Recrystallization Behavior of GH4096 Superalloy |
| LI Fulin, FU Rui, BAI Yunrui, MENG Lingchao, TAN Haibing, ZHONG Yan, TIAN Wei, DU Jinhui, TIAN Zhiling |
| 图14 细晶d4试样在1100℃、0.1 s-1，不同应变热压缩后显微组织的TEM像 |
| Fig.14 TEM images of fine grained d4 samples after hot compression at 1100oC, 0.1 s-1 and different engineering strains (SF—stacking fault) (a) 30% engineering strain (b) 50% engineering strain (c, d) 70% engineering strain |
|
|