弹性拉应力下Q235碳钢在5%NaCl盐雾中的成锈行为及其机理
Rust Formation Behavior and Mechanism of Q235 Carbon Steel in 5%NaCl Salt Spray Under Elastic Tensile Stress
弹性拉应力下Q235碳钢在5%NaCl盐雾中的成锈行为及其机理 |
| 李谦, 刘凯, 赵天亮 |
|
Rust Formation Behavior and Mechanism of Q235 Carbon Steel in 5%NaCl Salt Spray Under Elastic Tensile Stress |
| LI Qian, LIU Kai, ZHAO Tianliang |
| 图9 不同弹性拉应力水平的加载方式A和B下Q235碳钢在5%NaCl盐雾中暴露15 d后的EIS |
| Fig.9 Nyquist (a, d), Bode-impedance modulus (b, e), and Bode-phase angle (c, f) plots of Q235 carbon steel with loading modes A (a-c) and B (d-f) under various elastic tensile stress levels after exposed in 5%NaCl salt spray for 15 d (Zim—imaginary part of impedance, Zre—real component, |Z|—impedance modulus) |
|
|