以抗CMAS腐蚀为目标的稀土硅酸盐环境障涂层高熵化设计与性能提升
Rare Earth Silicate Environmental Barrier Coating Material: High-Entropy Design and Resistance to CMAS Corrosion
以抗CMAS腐蚀为目标的稀土硅酸盐环境障涂层高熵化设计与性能提升 |
| 王京阳, 孙鲁超, 罗颐秀, 田志林, 任孝旻, 张洁 |
|
Rare Earth Silicate Environmental Barrier Coating Material: High-Entropy Design and Resistance to CMAS Corrosion |
| WANG Jingyang, SUN Luchao, LUO Yixiu, TIAN Zhilin, REN Xiaomin, ZHANG Jie |
| 图4 四元(4RE1/4)2SiO5在1300℃下CMAS腐蚀50 h后样品表面XRD谱、腐蚀后样品表面形貌、腐蚀后样品截面残余CMAS析出空心棒状磷灰石形貌以及腐蚀后样品截面反应析出层放大图[ |
| Fig.4 XRD spectra (a, e), surface morphologies (b, f), and cross section morphologies (c, d, g, h) of (4RE1/4)2SiO5 after 50 h CMAS corrosion at 1300oC[ |
|
|