表面状态对核电关键材料腐蚀和应力腐蚀的影响
韩恩厚, 王俭秋

Effect of Surface State on Corrosion and Stress Corrosion for Nuclear Materials
HAN En-Hou, WANG Jianqiu
图4 电解抛光和SiO2机械抛光316L不锈钢样品在核电一回路高温高压水中腐蚀500 h后氧化膜的TEM分析[20]
Fig.4 TEM observations and analyses of the oxide scale formed on electropolished surface (EPS) (a, c) and colloidal silica slurry polished surface (CPS) (b, d) on 316L following the 500 h exposure in high temperature water[20]
(a, b) TEM images and corresponding SAED patterns (insets) showing the cross-section of the oxide scale and the area analyzed (c, d) EDS mappings for O, Ni, Cr, and Fe, respectively