Y对无取向6.5%Si钢凝固组织、中温压缩变形和软化机制的影响
Effect of Y on the Solidification Microstructure, Warm Compression Behavior, and Softening Mechanism of Non-Oriented 6.5%Si Electrical Steel
Y对无取向6.5%Si钢凝固组织、中温压缩变形和软化机制的影响 |
| 李民, 王继杰, 李昊泽, 邢炜伟, 刘德壮, 李奥迪, 马颖澈 |
|
Effect of Y on the Solidification Microstructure, Warm Compression Behavior, and Softening Mechanism of Non-Oriented 6.5%Si Electrical Steel |
| LI Min, WANG Jijie, LI Haoze, XING Weiwei, LIU Dezhuang, LI Aodi, MA Yingche |
| 图15 不同Y含量铸态试样500℃压缩后的TEM明场像和对应的SAED花样 |
| Fig.15 Dislocation configurations in bright-field TEM images (a-c) and the corresponding SAED patterns (d-f) along [001] zone axes of the as-cast 0Y (a, d), 0.017Y (b, e), and 0.15Y (c, f) samples after compression at 500oC |
|
|