镁合金抗高温氧化机理研究进展
Research Progress on the Mechanisms Controlling High-Temperature Oxidation Resistance of Mg Alloys
镁合金抗高温氧化机理研究进展 |
| 沈朝, 王志鹏, 胡波, 李德江, 曾小勤, 丁文江 |
|
Research Progress on the Mechanisms Controlling High-Temperature Oxidation Resistance of Mg Alloys |
| SHEN Zhao, WANG Zhipeng, HU Bo, LI Dejiang, ZENG Xiaoqin, DING Wenjiang |
| 图5 AZ91和AZ91-0.006%Be在400℃空气中氧化2 h后形成氧化膜的截面TEM明场像、HRTEM像、SAED花样及EDS分析[ |
| Fig.5 Cross-sectional TEM bright field images (a, e), HRTEM images (b, f), SAED patterns (c, g), and EDS analyses (d, h) of the oxide layers after 2 h oxidation at 400oC in air formed on AZ91 (a-d) and AZ91-0.006%Be (e-h)[ |
|
|